Accu-Tube's stainless steel, small diameter and hypodermic medical tubing technical information!

stainless steel tubing, small diameter tubing, hypodermic tube stainless steel tubing, small diameter tubing, hypodermic tube stainless steel tubing, small diameter tubing, hypodermic tube stainless steel tubing, small diameter tubing, hypodermic tube stainless steel tubing, small diameter tubing, hypodermic tube stainless steel tubing, small diameter tubing, hypodermic tube

Accu-Tube Corporation manufactures top quality standard and custom size stainless steel tubing. Sizes from small diameter hypodermic medical tubing .009" OD (.23mm) to .375"OD (9.35mm). Fabrication processes include welding, drawing, straightening, cutting, deburring, cleaning, bending, coiling, endforming, beading, flaring, swaging, and others.

stainless steel tubing, small diameter tubing, hypodermic tube


Click on the alloy that you wish to see the mechanical properties of and the link will take you there.
STAINLESS STEEL NICKEL ALLOY
304 Nickel 200 TM
304L Nickel 201 TM
316 Inconel 600 TM
316L
321
17-7PH TM



STAINLESS STEEL:

AUSTENITIC GRADES


MATERIAL UNS
NUMBER
CHEMICAL
COMPOSITION
(MAX. Unless indicated)
TYPICAL MECHANICAL PROPERTIES DESCRIPTION

304

To top of page
S30400
C	0.08
Mn	2.00
Si	1.00
P	0.045
S 	0.03
Cr	18.0-20.0
Ni	8.0-10.5
Ultimate tensile
(kpsi)

85-175*
Yield Strength
(kpsi)

40-145
Elongation
(% in 2")


50-8
Welding ease, good mechanical properties for long service, best for general all round corrosion resistance.




MATERIAL UNS
NUMBER
CHEMICAL
COMPOSITION
(MAX. Unless indicated)
TYPICAL MECHANICAL PROPERTIES DESCRIPTION

304L

To top of page
S30403
C	0.035
Mn       2.00
Si	1.00
P	0.045
S	0.03
Cr	18.0-20.0
Ni	8.0-13.0
Ultimate tensile
(kpsi)

85-175*
Yield Strength
(kpsi)

40-145
Elongation
(% in 2")


50-8
Very low carbon chromium nickel steel with general corrosion resistance similar to T304 but with superior resistance to intergranular corrosion following welding or stress relieving. It is recommended for parts which are fabricated by welding and which can not be subsequently annealed.

MATERIAL UNS
NUMBER
CHEMICAL
COMPOSITION
(MAX. Unless indicated)
TYPICAL MECHANICAL PROPERTIES DESCRIPTION

316

To top of page
S31008
C	0.08
Mn	2.00
Si	1.50
P	0.045
S 	0.03
Cr	16.0-18.0
Ni	10.0-14.0
Mo         2.0-3.0
Ultimate tensile
(kpsi)

85-165*
Yield Strength
(kpsi)

40-135
Elongation
(% in 2")


50-8
Chromium nickel stainless and heat resisting steel with superior corrosion resistance to other chromium nickel steels when exposed to many types of chemical corroders; superior creep strength at elevated temperatures. Uses: pressure gages, instruments exposed to chemicals, foods and pharmaceuticals.

MATERIAL UNS
NUMBER
CHEMICAL
COMPOSITION
(MAX. Unless indicated)
TYPICAL MECHANICAL PROPERTIES DESCRIPTION

316L

To top of page
S31603
C	0.035
Mn	2.00
Si	1.00
P	0.045
S 	0.03
Cr	16.0-18.0
Ni	10.0-14.0
Mo         2.0-3.0
Ultimate tensile
(kpsi)

85-165*
Yield Strength
(kpsi)

40-135
Elongation
(% in 2")


50-8
Low carbon chromium nickel stainless steel with general corrosion resistance similar to type 316 but with superior resistance to intergranular corrosion following welding or stress relieving. It is recommended for use in parts which are fabricated by welding and which cannot be subsequently annealed.

MATERIAL UNS
NUMBER
CHEMICAL
COMPOSITION
(MAX. Unless indicated)
TYPICAL MECHANICAL PROPERTIES DESCRIPTION

321

To top of page
S32100
C	0.08
Mn	2.00
Si	1.00
P	0.045
S 	0.03
Cr	17.0-19.0
Ni	9.0-12.0
Ti	(note A)
Ultimate tensile
(kpsi)

85-165*
Yield Strength
(kpsi)

40-135
Elongation
(% in 2")


50-8
Chromium nickel steel containing titanium which is recommended for parts fabricated by welding which cannot be subsequently annealed. Also recommended for parts to be used at temperatures between 800F deg and 1650F degrees.

STAINLESS STEEL:

PRECIPITATION HARDENING GRADES


MATERIAL UNS
NUMBER
CHEMICAL
COMPOSITION
(MAX. Unless indicated)
TYPICAL MECHANICAL PROPERTIES DESCRIPTION

17-7 PH

TM
(Registered
Trademark of
Armco Steel )
To top of page
S17700
C	0.09
Mn	1.00
Si	1.00
P	0.045
S	0.03
Cr	16.0-18.0
Ni	6.50-7.75
Al	.75-1.50
Ultimate tensile
(kpsi)

130-230 (note D)
Yield Strength
(kpsi)

40-220 (note D)
Elongation
(% in 2")


30-1 (note D)
A chromium nickel stainless steel with characteristics of good workability, easy hardening, high strength, and excellent mechanical properties at elevated temperatures, can be heat treated at relatively low temperatures for high strength properties.


NICKEL ALLOYS:


     

MATERIAL UNS
NUMBER
CHEMICAL
COMPOSITION
(MAX. Unless indicated)
TYPICAL MECHANICAL PROPERTIES DESCRIPTION

Nickel 200

TM
(Registered Trademark of Huntington Alloys)
To top of page
N02200
C	0.15
Mn	0.35
Si	0.35
Cu	0.25
Fe	0.40
Ni + Co	99 Min.
Ultimate tensile
(kpsi)

65-100*
Yield Strength
(kpsi)

15-90
Elongation
(% in 2")


45-6
Commercially pure nickel. High corrosion resistance. Used in food handling and electronics.

MATERIAL UNS
NUMBER
CHEMICAL
COMPOSITION
(MAX. Unless indicated)
TYPICAL MECHANICAL PROPERTIES DESCRIPTION

Nickel 201

TM
(Registered Trademark of Huntington Alloys)
To top of page
N02201
C	0.02
Mn	0.35
Si	0.35
Cu	0.25
Fe	0.40
Ni + Co	99 Min.
Ultimate tensile
(kpsi)

65-100*
Yield Strength
(kpsi)

15-90
Elongation
(% in 2")


45-6
Similar to Ni 200 except with a lower carbon content for better formability. Most applications in chemicals

MATERIAL UNS
NUMBER
CHEMICAL
COMPOSITION
(MAX. Unless indicated)
TYPICAL MECHANICAL PROPERTIES DESCRIPTION

Inconel 600

TM
(Registered Trademark of Huntington Alloys)
To top of page
N06600
C	0.15
Mn	1.00
Si	0.50
Cu	0.50
Fe	6.0-10.0
Ni + Co	72 Min
Cr	14.0-17.0
S	0.015
Ultimate tensile
(kpsi)

90-145*
Yield Strength
(kpsi)

40-120
Elongation
(% in 2")


40-6
Outstanding corrosion resistance with excellent workability. Good for cryogenic to high temperature applications up to 2000F degrees.


Notes:
A) Type 321 shall have a titanium content of not less than five times the carbon content and not more than .70%.
C) Type 409 shall have a titanium content of not less than six times the carbon content and not more than .75.
D) Dependent on degree of cold work, final size, and heat treat.
* Dependent on degree of cold work and final size.

To top of page

Accu-Tube Corporation

MAILING ADDRESS:
Accu-Tube Corporation
2960 South Umatilla Street
Englewood, Colorado 80110
USA

Phone: (303) 761-2258
Fax: (303) 761-2276
E-MAIL: accutube@accutube.com


Home | Alloys | Product Info. | Technical Info. | Stock Sizes | Fabrication Info. | E-mail Accu-Tube

This page was created with pride by - John Bourque